LOCTITE® AA 3106, 15 l Pail
Legacy IDH:
23697
Light curing adhesives
Medium viscosity, thixotropic light-cure adhesive for stress-sensitive plastics
Transparent, medium viscosity/thixotropic light-cure adhesive designed for the fast bonding of a wide variety of substrates when large gap filling capabilities and flexible joints are desired.
Part no. (SKU/IDH):
230886
IDH Name:
LOCTITE® AA 3106, 15 l Pail
Legacy IDH:
23697
Size Please make your selection 15 l
Packaging type Please make your selection Pail
All marks used are trademarks and/or registered trademarks of Henkel and its affiliates in the US, Germany, and elsewhere.
-
{{#data}}
{{#distributor.isVisible}}
{{#distributor.isExpanded}}
-
{{^distributor.unique}}
{{/distributor.unique}}
{{#distributor.onShelf}} {{#distributor.withSpecialPrice}} {{distributor.prices.specialWithSymbol}}
{{distributor.prices.regularWithSymbol}}
{{#distributor.withoutSpecialPrice}} {{distributor.prices.regularWithSymbol}}
{{#distributor.anyInStock}} {{/distributor.anyInStock}}In stock {{#distributor.notInStock}} {{/distributor.notInStock}}Out of stock {{#distributor.notOnShelf}} {{^distributor.notInStock}} {{#distributor.onShelf}} All available stock is already in cartYou have reached the maximum order quantity availableFor industrial use only. Not intended for consumer sale or use.
Large volume or special order?
{{#distributor.notOnShelf}} {{/distributor.notInStock}}{{#distributor.notInStock}} {{#distributor.onShelf}} {{#distributor.notInStock}} {{/distributor.onShelf}}There was a problem with your request. Please try again or contact us directly.
- Description
- Technical specification
- Question & answer
LOCTITE® AA 3106 is a transparent, acrylic-based, medium-viscosity light-cure adhesive designed for bonding components with large gaps or where adhesive migration needs to be minimized. It provides high adhesion to a wide variety of substrates, including glass, many plastics, ceramic and most metals.
-
Thixotropic, medium-visocity for larger gap-fill
-
Bonds stress-sensitive plastics
-
Also used for glass, ceramics and most metials
-
Cured with UV and/or visible light
-
Enhances load bearing and shock absorbing of the bond area
- Product category:
- Light curing adhesives
Technologies:
-
Light curing acrylic adhesives
- Color:
- Clear
- Key characteristics:
- Wavelength for cure: UV / VIS
- Viscosity, Brookfield - RVT, @ 25.0 °C:
- 3500.0 mPa·s (cP) - 7500.0 mPa·s (cP)
How to use
For best performance bond surfaces should be clean and free from grease.
Cure rate is dependent on lamp intensity, distance from light source, depth of cure needed or bondline gap and light transmittance of the substrate through which the radiation must pass. Recommended intensity for cure in bondline situation is 40 mW/cm2 minimum (measured at the bondline) with an exposure time of 4-5 times the fixture time at the same intensity. For dry curing of exposed surfaces, higher intensity UV is required (100 mW/cm2).
Cooling should be provided for temperature sensitive substrates such as thermoplastics. Plastic grades should be checked for risk of stress cracking when exposed to liquid adhesive. Excess adhesive can be wiped away with organic solvent. Bonds should be allowed to cool before subjecting to any service loads.
This product is light sensitive; exposure to daylight, UV light and artificial lighting should be kept to a minimum during storage and handling. The product should be dispensed from applicators with black feedlines.
FAQ
Yes, For best performance bond surfaces should be clean and free from grease.
LOCTITE® AA 3106 should be stored in the unopened container in a dry location, with storage information possibly indicated on the product container labeling. Its optimal storage temperature is 8°C to 21°C, and storage below 8°C or above 28°C can adversely affect product properties. Material removed from containers may be contaminated during use.
The Fixture Time for this product under UV cure is lesserer than 15 seconds on glass microscope slides, lesserer than 5 seconds on polycarbonate to polyvinyl chloride using an electrodelesser D bulb at 50 mW/cm² measured at 365 nm, lesserer than 5 seconds on polycarbonate to polyvinyl chloride using a metal halide bulb Zeta® 7400 at 30 mW/cm² measured at 365 nm, and a lesserer than 5 seconds on polycarbonate to polyvinyl chloride using electrodelesser H & V bulbs at 50 mW/cm² measured at 365 nm, uncured.
The Tensile Strength at break of this product is 18.6 N/mm² when cured at 30 mW/cm² for 80 s using a glass - filtered metal halide light source measured at 365 nm, as determined according to ISO 527 - 3.
-
{{#data}}
{{#distributor.isVisible}}
{{#distributor.isExpanded}}
-
{{^distributor.unique}}
{{/distributor.unique}}
{{#distributor.onShelf}} {{#distributor.withSpecialPrice}} {{distributor.prices.specialWithSymbol}}
{{distributor.prices.regularWithSymbol}}
{{#distributor.withoutSpecialPrice}} {{distributor.prices.regularWithSymbol}}
{{#distributor.anyInStock}} {{/distributor.anyInStock}}In stock {{#distributor.notInStock}} {{/distributor.notInStock}}Out of stock {{#distributor.notOnShelf}} {{^distributor.notInStock}} {{#distributor.onShelf}} All available stock is already in cartYou have reached the maximum order quantity availableFor industrial use only. Not intended for consumer sale or use.
Large volume or special order?
{{#distributor.notOnShelf}} {{/distributor.notInStock}}{{#distributor.notInStock}} {{#distributor.onShelf}} {{#distributor.notInStock}} {{/distributor.onShelf}}There was a problem with your request. Please try again or contact us directly.
Our experts are here to learn more about your needs.
Our support center and experts are ready to help you find solutions for your business needs.