Structural adhesives
Multi-substrate adhesive for superior thermal shock resistance
This 2-part industrial-grade adhesive cures at room temperature to form a tough bond line with excellent resistance to peel and impact forces.
-
LOCTITE® EA E-120HP, 400 ml Dual cartridge en_GLIDH: 237130
-
LOCTITE® EA E-120HP, 400 ml Dual cartridge en_GLLOCTITE EA E-120HP A RESIN known as DB EPX ADH E-120HP 400 ML. RES (702025)IDH: 237130
-
LOCTITE® EA E-120HP, 400 ml Dual cartridge en_GLLOCTITE EA E-120HP known as DB EPOXY ADH E-120HP 400 ML. (702026)IDH: 237130
-
LOCTITE® EA E-120HP, 400 ml Dual cartridge en_GLLOCTITE EA E-120HP A RESIN known as DB EPX ADH E-120HP 400 ML. RES (702025)IDH: 237130
-
LOCTITE® EA E-120HP, 400 ml Dual cartridge en_GLIDH: 237130
-
LOCTITE® EA E-120HP, 400 ml Dual cartridge en_GLLOCTITE EA E-120HP known as DB EPOXY ADH E-120HP 400 ML. (702026)IDH: 237130
Size Please make your selection
Packaging type Please make your selection
All marks used are trademarks and/or registered trademarks of Henkel and its affiliates in the US, Germany, and elsewhere.
-
{{#data}}
{{#distributor.isVisible}}
{{#distributor.isExpanded}}
-
{{^distributor.unique}}
{{/distributor.unique}}
- Description
- Technical specification
LOCTITE® EA E-120HP is a 2-part, high-viscosity, industrial-grade epoxy adhesive with extended work life. Once mixed, it cures at room temperature to form a tough bond line with excellent resistance to peel and impact forces. You can also expect superior thermal shock resistance, excellent mechanical and electrical properties, and resistance to a wide variety of solvents and chemicals. Ideal for bonding nose cones in aerospace applications, as well as low stress, general industrial applications requiring high impact- and high peel strength. It bonds dissimilar materials including aluminium, steel and other metals, as well as a variety of plastics and ceramics.
-
Multi-substrate structural bonder
-
Resistant to peel and impact forces
-
120-minute work time allows for adjustments
-
Resistant to solvents and chemicals
-
Bonds dissimilar materials
- Product category:
- Structural adhesives
Technologies:
-
Electronics assembly materials
-
2C general epoxy
- Applications:
- Bonding plastic; Structural bonding
- Cure type:
- Room temperature (ambient) cure
- FEA (finite element analysis):
- Finite strain; Viscoelastic
- Hardener: Colour:
- Amber
- Key characteristics:
- Shock resistant; Viscosity: high viscosity; Work life: extended work life
- Mix ratio, by volume:
- 2 : 1
- Mix ratio, by weight:
- 100 : 46
- Mixed: Colour:
- Beige
- Number of components:
- 2 part
- Recommended for use with:
- Ceramic; Metal: aluminium; Metal: steel; Plastic
- Resin: Colour:
- Beige
How to use
For best performance, part surfaces should be clean and free from grease. For high-strength structural bonds, remove surface contaminants such as paint, oxide films, oils, dust, mould release agents and all other surface contaminants.
For dual cartridges, insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Remove the cartridge cap and expel a small amount of adhesive to ensure that both sides are flowing evenly and freely. If automatic mixing of the resin and hardener is required, attach the mixing nozzle to the cartridge and begin dispensing the adhesive. For hand mixing, dispense the required amount of adhesive and mix thoroughly, continuing for approximately 15 seconds after a uniform colour is achieved. For bulk containers, mix thoroughly by weight or volume in the proportions specified in the Product Description section, mixing vigorously for approximately 15 seconds after a uniform colour is obtained. Do not mix quantities greater than 4 kg, as excessive heat build-up may occur; mixing smaller quantities will help minimise heat build-up.
Apply the adhesive as quickly as possible after mixing to one surface to be joined. For maximum bond strength apply adhesive evenly to both surfaces. Parts should be assembled immediately after mixed adhesive has been applied.
Keep assembled parts from moving during cure. The bond should be allowed to cure for 24 hours before subjecting it to any service loads. Where necessary curing can be accelerated by the application of moderate heat at the bond line - refer to the Technical Data Sheet for cure recommendations.
FAQ
Yes. For best performance, part surfaces should be clean and free from grease. For high-strength structural bonds, remove surface contaminants such as paint, oxide films, oils, dust, mould release agents and all other surface contaminants.
LOCTITE® EA E-120HP should be stored in an unopened container in a dry location, as indicated on the product container labelling, with an optimal storage temperature range of 8°C to 21°C. Storage below 8°C or above 28°C can adversely affect product properties. Material removed from the container may become contaminated during use and should not be returned to the original container.
The tensile strength of this product is 41 N/mm², measured under ISO 527-3, and in the cured state at 22°C for 7 days.
LOCTITE® EA E-120HP will be recommended for applications which require high-strength, rigid bonding with resistance to elevated temperatures, ensuring reliability and safety under extreme conditions.