Retaining compounds
High strength, slow-curing retaining compound for close-fitting cylindrical parts
Low viscosity, high-strength slow-curing retaining compound for assembly of cylindrical components. Ideal for interference fits or close-fitting slip fits.
All marks used are trademarks and/or registered trademarks of Henkel and its affiliates in the US, Germany, and elsewhere.
- Description
- Technical specification
When you need a low viscosity, slow-curing retaining compound for your press fitted or close-fitting cylindrical parts, consider LOCTITE® 675. It has very low viscosity, high strength, and a slow cure (fixture time on steel is 45 minutes), and a maximum diametrical clearance of 0.1 mm (0.0004"). Perfect for filling inner voids in close fitting press fits, keyways, and splines; mounting bearings and bushings, and making press fits even stronger. Service temperature is -55°C to 150°C (-67°F to 302°F). Also for use on Mil-R-46082 military specifcation related applications.
-
High shear strength
-
Very low viscosity
-
Slow curing
-
Ideal for press fitted or close-fitting slip fitted cylindrical parts
-
Meets Mil Spec: Mil-R-46082
- Product category:
- Retaining compounds
Technologies:
-
Acrylates, anaerobic cure
- Chemical basis / base:
- Methacrylate
- Color:
- Green
- Diametrical clearance:
- < 0.1 mm
- Fixture time:
- 45.0 min.
- Recommended for use with:
- Metal: steel
- Shear strength:
- 20.0 N/mm²
- Viscosity, Brookfield - RVT, Spindle 1, speed 50 rpm:
- 100.0 mPa·s (cP) - 150.0 mPa·s (cP)