Wear resistant coatings
Wear prevention - low friction, brushable, easy to use, corrosion-resistant
Designed to rebuild and repair processing equipment with a brushable, ultra-smooth, low friction coating, protecting equipment from corrosion and wear.
All marks used are trademarks and/or registered trademarks of Henkel and its affiliates in the US, Germany, and elsewhere.
- Description
- Technical specification
LOCTITE® PC 7227 Nordbak® Brushable Ceramic Wear Prevention Coating is a low friction, brushable, easy-to-use epoxy resin system that offers protection against turbulence, chemical attack, abrasion, and corrosion. The high gloss, low friction coating can be used to restore or increase pump efficiency. It can also be used to repair and protect heat exchanges and condensers, lining tanks, pipes and chutes, resurfacing and repairing rudders and pintel housings, and resurfacing cooling pump impellers and butterfly valves.
-
Self-leveling, smooth low surface-energy coating
-
Protects against abrasion, corrosion, wear and damage from turbulence
-
Brushable and easy to mix and apply
-
Can use as topcoat over LOCTITE Wearing Compounds for applications requiring surface rebuilding/protection
- Product category:
- Wear resistant coatings
Technologies:
-
Thermosets, 2K general epoxy
-
Specialties, others
- Color:
- Gray
- Drying time:
- 6.0 hr.
- Mix ratio, by volume:
- 2.75 : 1
- Particle size:
- Fine
How to use
Remove dirt, oil, grease, loose flaky rust, etc., with a suitable high pressure water cleaning system using LOCTITE® SF 7840 cleaner/degreaser.
Blast all surfaces to be coated, with a sharp edged angular grit, such as aluminum oxide, to a depth of profile of approximately 75 microns, and a degree of cleanliness of Very Thorough Blast Cleaning/Near White Metal (ISO 8501-1 SA 2½ /SSPC-SP 10).
After blasting, metal surfaces should be cleaned with a waterless, or solvent based LOCTITE® cleaner, such as LOCTITE SF 7611 or SF 7633, and allow the surface to dry before application of the product. Coat the surface before any oxidation or contamination takes place.
To avoid flash rust, repairs should be made as soon as possible or within a maximum 2 hours of blasting. Otherwise, apply a thin coat of LOCTITE SF 7515 to all surfaces and allow to react for 1 minute. After 1 minute, blow off with clean and dry compressed air until the surface is completely dry.
Measure 4.8 parts of resin and 1 part of hardener by weight or mix entire kit thoroughly until color is consistent.
Brush apply fully mixed material to prepared surface by first forcing a thin layer deep into the texture of the substrate. Then immediately build up to the desired finished thickness of 250 to 500 microns (10 to 20 mils) per coat with a minimum of 2 coats to avoid any pin holes. Working and cure time depend on temperature and mass - the higher the temperature and the larger the mass, the faster the cure.
Visually inspect for pinholes and misses just after application. Once the coating has cured, repeat visual inspection to confirm absence of pinholes, voids or damaged areas.
FAQ
It is recommended to apply this product at 500 to 1000 microns (20 to 40 mils) in a minimum of two coats of 250 to 500 microns (10 to 20 mils) each to avoid pin holes.