Part no. (SKU/IDH):
2063041
IDH Name:
LOCTITE® EA 3425, Mixed, 50 ml Dual cartridge
Structural adhesives
High-strength, thixotropic structural bonder for magnets
A 2-part, high-strength, thixotropic structural adhesive for SPM and IPM bonding.
Part no. (SKU/IDH):
2063041
IDH Name:
LOCTITE® EA 3425, Mixed, 50 ml Dual cartridge
Size Please make your selection 50 ml
All marks used are trademarks and/or registered trademarks of Henkel and its affiliates in the US, Germany, and elsewhere.
-
{{#data}}
{{#distributor.isVisible}}
{{#distributor.isExpanded}}
- {{^distributor.unique}} {{/distributor.unique}} {{/distributor.isExpanded}} {{^distributor.isExpanded}} {{/distributor.isExpanded}} {{/distributor.isVisible}} {{/data}}
- Description
- Technical specification
LOCTITE® EA 3425 is a white to yellow (after mixing) epoxy structural adhesive system that offers high impact and high humidity resistance and very high shear strength of 27 N/mm². Its thixotropic nature makes it easy to apply and reduces liquid migration after application, making it ideal for gap-filling (up to 3 mm) and use on vertical surfaces. It’s typically used for surface permanent magnet (SPM) and interior permanent magnet (IPM) bonding where high production cycling is required. LOCTITE EA 3425 cures at room temperature when exposed to RT, heat or induction and exhibits a high modulus of elasticity and good chemical resistance.
-
High strength
-
Non-sagging
-
Resistant to impact, moisture and chemicals
-
Temperature-resistant up to 120°C (248°F)
- Product category:
- Structural adhesives
Technologies:
-
Thermosets, 2K general epoxy
- Fixture time:
- 240.0 min.
- Hardener: Color:
- Beige
- Hardener: Specific gravity, @ 25.0 °C:
- 1.37 - 1.45
- Hardener: Viscosity, Brookfield - RVT, @ 25.0 °C:
- 100000.0 mPa·s (cP) - 300000.0 mPa·s (cP)
- Mix ratio, by volume:
- 1 : 1
- Mixed: Color:
- White; Yellow
- Resin: Color:
- Beige
- Resin: Specific gravity, @ 25.0 °C:
- 1.34 - 1.4
- Resin: Viscosity, Brookfield - RVT, @ 25.0 °C:
- 1500000.0 mPa·s (cP) - 3500000.0 mPa·s (cP)
-